Spectrophotometric evaluation of calcium ion release from different calcium hydroxide preparations: An in-vitro study.

Atul Jain, Kanchan Bhadoria, Hemendra Singh Hada


Introduction: Infections and conditions involving the pulp tissue have been treated with Calcium hydroxide (CaOH) since long. In the last decade, use of Mineral trioxide aggregate (MTA) has gained ground. This study was carried out to comparatively evaluate the Ca release from CaOH powder with different vehicles and different types of MTA. Materials and Methods: 40 single rooted mandibular premolars were selected, decoronated and biomechanically prepared. They were randomly divided into four groups, consisting of 10 samples each. Root canals were packed with different preparations of CaOH and MTA. Ca ion released was evaluated with an UV-spectrophotometer. Result: Amongst the CaOH preparations, propylene glycol as a vehicle produced extended release of Ca ion (7.3410±.01135) for a period of 14 days. Whereas, amongst MTA based products, MTA angelus produced maximum Ca ions release (2.4240±.01075). Statistically significant difference was present between the four groups (p<0.05). Conclusion: Propylene glycol mixed with CaOH powder, produces higher and extended release of Ca ions than distilled water. MTA angelus produces better and consistent Ca ion release.


Calcium Hydroxide; Propylene glycol; Pulp capping and pulpectomy agents; Solubility.


Murvindran V, James D R. Antibiotics as an Intracanal Medicament in Endodontics. J Pharm Sci Res. 2014;6(9):297–301.

Fava LR, Saunders WP. Calcium hydroxide pastes: classification and clinical indications. Int Endod J. 1999;32(4):257–82.

Grover C, Shetty N. Evaluation of calcium ion release and change in pH on combining calcium hydroxide with different vehicles. Contemp Clin Dent. 2014;5(4):434–9.

Pires-de-Souza Fde C, Moraes PC, Garcia Lda F, Aguilar FG, Watanabe E. Evaluation of pH, calcium ion release and antimicrobial activity of a new calcium aluminate cement. Braz Oral Res. 2013;27(4):324–30.

Neelakantan P, Grotra D, Sharma S. Retreatability of 2 mineral trioxide aggregate-based root canal sealers: a cone-beam computed tomography analysis. J Endod. 2013;39(7):893–6.

Fulzele P, Baliga S, Thosar N, Pradhan D. Evaluation of calcium ion, hydroxyl ion release and pH levels in various calcium hydroxide based intracanal medicaments: An in vitro study. Contemp Clin Dent. 2011;2(4):291–5.

de Andrade Ferreira FB, Silva E Souza Pde A, do Vale MS, de Moraes , IG , Granjeiro JM. Evaluation of pH levels and calcium ion release in various calcium hydroxide endodontic dressings. Oral Surg Oral Med Oral Pathol Oral Radiol Endod. 2004;97(3):388–92.

Bayram HM, Bayram E, Atakol O. Atomic absorption spectrometry evaluation of calcium ion release from different calcium silicate-based endodontic materials used with new irrigants. Biomed Res. 2016;(Special Issue):S333–6.

Larsen MJ, Hörsted-Bindslev P. A laboratory study evaluating the release of hydroxyl ions from various calcium hydroxide products in narrow root canal-like tubes. Int Endod J. 2000;33(3):238–42.

Gandolfi MG, Siboni F, Primus CM, Prati C. Ion release, porosity, solubility, and bioactivity of MTA Plus tricalcium silicate. J Endod. 2014;40(10):1632–7.

Salehimehr G, Nobahar S, Hosseini-Zijoud SM, Yari S. Comparison of physical & chemical properties of Angelus MTA and new endodontic restorative material. J App Pharm Sci. 2014;4(7):105–9.

Full Text: PDF


  • There are currently no refbacks.

Creative Commons License
This work is licensed under a Creative Commons Attribution 3.0 License.

Corresponding: Facultad de Odontología, Universidad de Concepción, Chile. Roosevelt 1550, Concepción, Chile. Phone +56-41-2204232 - E-mail journal@joralres.com.